PRIMACOR 1410
PRIMACOR™ 1410 Copolymer is an ethylene acrylic acid copolymer suitable for monolayer or coextrusion blown films. PRIMACOR™ 1410 Copolymer has been specifically designed for use as a heat seal or adhesive layer in composite films.
Introduction
PRIMACOR™ 1410 Copolymer is an ethylene acrylic acid copolymer suitable for monolayer or coextrusion blown films. PRIMACOR™ 1410 Copolymer has been specifically designed for use as a heat seal or adhesive layer in composite films.
PRIMACOR™ 1410 Copolymer exhibits:
· Excellent hot tack and sealability
· Excellent toughness and strength
· Excellent crack resistance
· Insensitivity to moisture
· Good optical properties
Parameters
| Nominal Value (English) | Nominal Value (SI) | Test Method | ||
| Resin Properties |
Density | 0.938 g/cm3 | 0.938 g/cm3 | ASTM D792
ISO 1183 |
| Melt Index (2.16 kg @190℃) | 1.5 g/10min | 1.5 g/10min | ASTM D1238 ISO 1133 |
|
| Comonomer Content | 9.7 % | 9.7 % | SK Method | |
| Vicat Softening Temperature | 178 ℉ | 81.1 ℃ | ASTM D1525
ISO 306 |
|
| Melting Temperature (DSC) | 208 ℉ | 97.8 ℃ | SK Method | |
| Film
Properties |
Film Thickness | 2.0 mil | 50.8 μm | ASTM D374 |
| Dart Impact Strength | 580 g | 580 g | ASTM D1709B
ISO 7765-1/B |
|
| Haze | 5.8 % | 5.8 % | ASTM D1003
ISO 14782 |
|
| Gloss (45°) | 65 | 65 | ASTM D2457 | |
| Elmendorf Tear Strength MD
Elmendorf Tear Strength TD |
380 g
510 g |
380 g
510 g |
ASTM D1922
ISO 6383-2 |
|
| Tensile Strength at Yield MD
Tensile Strength at Yield TD |
1710 psi
1590 psi |
11.8 MPa
10.9 MPa |
ASTM D882
ISO 527-3 |
|
| Tensile Strength at Break MD
Tensile Strength at Break TD |
5500 psi
5530 psi |
37.9 MPa
38.1 MPa |
ASTM D882
ISO 527-3 |
|
| Tensile Elongation at Break MD
Tensile Elongation at Break TD |
400 %
470 % |
400 %
470 % |
ASTM D882
ISO 527-3 |
|
| Extrusion
Condition 3 |
· Screw Size: 2.5 in. (63.5 mm); 30:1 L/D; Single Flight with Maddock Mixer · Die Gap: 40 mil (1.0 mm)
· Die Diameter: 6 in. (152.4 mm) · Melt Temperature: 385 ℉ (196 ℃) · Output: 6 lb/hr/in. of Die Circumference (1.07 kg/hr/cm of Die Circumference) · Blow-up Ratio: 2.5:1 · Frost Line Height: 29 in. (737 mm) |
|||
1 Comonomer content measured by a SK proprietary method that has equivalent accuracy as compared to ASTM D 4094.
2 Equipment used to process this resin should be constructed of corrosion resistant materials. Dies and adapters are recommended to be stainless steels and/or duplex chrome or nickel plated.
Application
· Specialty and skin packaging
· Multilayer films
Extrusion Notes
Equipment used to process this resin should be constructed of corrosion resistant materials. Dies and adapters are
recommended to be stainless and/or duplex chrome or nickel plated.
Notes
These are typical values and are not be construed as specifications. The physical properties are highly dependent on the
manufacturing conditions. So customers should confirm performances by their own tests.