ENGAGE™ 8200
ENGAGE™ 8200 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications.
Introduction
ENGAGE™ 8200 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer applications.
ENGAGE™ 8200 provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE), especially in applications requiring slightly higher melt flow.
ENGAGE™8200 also provides high filler loading capability, excellent electrical properties, and (when cross-linked) exceptional heat aging, compression set, and weather resistance properties.
Parameters
| Nominal Value (English) | Nominal Value (SI) | Test Method | ||
| Physical | Density | 0.870 g/cm3 | 0.870 g/cm3 | ASTM D792 |
| Melt Index (190℃/2.16 kg ) | 5.0 g/10min | 5.0 g/10min | ASTM D1238 | |
| Mooney Viscosity (ML 1+4, 250°F(121℃)) | 8 MU | 8 MU | ASTM D1646 | |
| Mechanical | Tensile Modulus-100% Secant1 (Compression Molded) |
334 psi | 5.70 MPa | ASTM D638 |
| Tensile Strength1 (Break, Compression Molded) |
827 psi | 27.9 MPa | ASTM D638 | |
| Tensile Elongation 1
(Break, Compression Molded) |
1100 % | 1100 % | ASTM D638 | |
| Flexural Modulus
1% Secant : Compression Molded 2% Secant : Compression Molded |
1580 psi
1570 psi |
10.9 MPa
10.8MPa |
ASTM D790 | |
| Elastomers | Tear Strength 2 | 212 lbf/in | 37.1 kN/m | ASTM D624 |
| Hardness | Durometer Hardness
Shore A, 1 sec, Compression Molded Shore D, 1 sec, Compression Molded |
66
17 |
66
17 |
ASTM D2240 |
| Thermal | Glass Transition Temperature | -63.4 °F | -53.0 ℃ | Dow Method |
| Vicat Softening Temperature | 98.6 °F | 37.0 ℃ | ASTM D1525 | |
| Melting Temperature (DSC) 3 | 138 °F | 59.0 ℃ | Dow Method | |
| Peak Crystallization Temperature (DSC) | 111 °F | 44.0 ℃ | Dow Method |
Notes
These are typical properties only and are not to be construed as specifications. Users should confirm resuits by their own tests.
1 20 in/min (510 mm/min)
2 Die C
3 10°C/min
Application
- General purpose thermoplastic elastomers
- Impact modification
- Wire and cable
Features
- Pellet form
- Excellent flow characteristics
- High filler loading
- Excellent electrical properties
- Improved impact in polypropylene and polyethyleneE
- xceptional heat aging,compression set,and weather resistance when cured
| Minimum Order Quantity: | 25kg |
| Price: | $1.5-$3 |
| Packaging Details: | 25kg/bag |
| Delivery Time: | 3-5 working days to departure port |
| Payment Terms: | TT/LC |
| Supply Ability: | 1000MT/Month |