EAA 5100
Escor™ 5100 resin is primarily intended for extrusion coating, coextrusion coating, and extrusion lamination. Escor™ 5100 resin offers the following advantages: excellent adhesion to polar substrates, aluminum foil, metallized films, paper, iron, steel, and glass; high bond resistance when used to pack acidic food products
Introduction
ESCOR™ 5100 resin is primarily intended for extrusion coating, coextrusion coating, and extrusion lamination.ESCOR™ 5100 resin offers the following advantages: excellent achesion to polar substrates,aluminum foil, metallized fims, paper iron, steel, and glass; high bond resistance when used to pack acidic food products; excellent coextrusion adhesive resin for polyamides; outstanding sealing performance, very low temperature sealing with high strength; and high hot tack forces and good seal throgh contamination.
Main Grades
| Resin Properties | Typical Value ( English ) | Typical Value ( SI ) | Test Based On |
| Density | 0.940 g/cm3 | 0.940 g/cm3 | ASTM D1505 |
| Melt Index 2 ( 190℃/2.16 kg ) | 8.5 g/10 min | 8.5 g/10 min | ASTM D1238 |
| Acrylic Acid Content | 11.0 wt% | 11.0 wt% | ExxonMobil Method |
| Peak Melting Temperature | 204 ℉ | 95 ℃ | ExxonMobil Method |
| Draw Down
Constant output at 35 rpm, 536℉（280℃） |
230 m/min | 230 m/min | ExxonMobil Method |
| Neck-in
82 ft/min(25 m/min), Constant output at |
4.0 in | 10 cm | ExxonMobil Method |
| 164 ft/min(50 m/min), Constant output at 35 rpm, 536 ℉ ( 280℃ ) |
2.1 in | 5.3 cm | |
| 328 ft/min(100 m/min), Constant output at 35 rpm, 536 ℉ ( 280℃ ) |
1.5 in | 3.7 cm |
Application
- Food packages
- Extrusion Coating
Features
- High hot tack forces
- Good seal through contamination.
Parameters
| Minimum Order Quantity: | 25kg |
| Price: | $2-$5 |
| Packaging Details: | 25kg/bag |
| Delivery Time: | 3-5 working days to departure port |
| Payment Terms: | TT/LC |
| Supply Ability: | 1000MT/Month |