AFFINITY™ PF 1140G

High performance blown film resin for flexible packaging, excellent abuse resistance, low temperature seal initiation, excellent optics, outstanding high oxygen transmission rates.

Category:
Description

Overview

AFFINITY* PF 1140G Polyolefin Plastomer (POP) is produced via lNSITE* Technology. lt is an ethylene alpha-olefin resin designed to be used in a variety of demanding applications including fom-fill-seal packaging and fresh producebags. This resin has excellent compatibility with other polyolefins, allowing efficient blending and coextrusion.

  • High performance blown film resin for flexible packaging
  • Excellent abuse resistance
  • Low temperature seal initiation
  • Excellent optics
  • Outstanding high oxygen transmission rates

Complies with:

  • U.S.FDA FCN 424
  • Canadian HPFP No Objections
  • EU. NO 10/2011
  • U.S.FDA-DMF

Consult the regulations for complete details.

Additive

  • Antiblock: No
  • Slip: No
  • Processing Aid: No

Properties

 

    Nominal Value(English)         Nominal Value(SI)     Test Method
 Physical  Density 0.897 g/cm3 0.897 g/cm3 ASTM D792
 Melt index (190℃/2.16kg) 1.6 g/10 min 1.6 g/10 min ASTM D1238
 Films  Film Thickness – Tested 2.0 mil 51 μm
 Film Puncture Energy (2.0 mil(51 μm)) 72.4 in · lb 8.18 J Dow Method
 Film Puncture Force (2.0 mil(51 μm)) 18.8 lbf 83.6 N Dow Method
 Film Puncture Resistance (2.0 mil(51 μm)) 245 ft · b/in3 20.3 J/cm3 Dow Method
 Secant Modulus

2% Secant, MD : 2.0 mil(51 μm)

2% Secant, TD : 2.0 mil(51 μm)

 10600 psi

10600 psi

 72.8 MPa

73.2 MPa

 ASTM D882
 Tensile Strength

MD: Yield, 2.0 mil(51 μm)

TD: Yield, 2.0 mil(51 μm)

MD: Break, 2.0 mil(51 μm)

TD: Break, 2.0 mil(51 μm)

 840 psi

920 psi

7290 psi

5730 psi

 5.79 MPa

6.34 MPa

50.3 MPa

39.5MPa

 ASTM D882
 Tensile Elongation

MD: Break, 2.0 mil(51 μm)

TD: Break, 2.0 mil(51 μm)

 690 %

700 %

 690 %

700 %

 ASTM D882
 Dart Drop Impact 2.0 mil(51 μm) ＞ 850 g ＞ 850 g    ASTM D1709B
 Elmendorf Tear Strength1

MD : 2.0 mil(51 μm)

TD : 2.0 mil(51 μm)

 470 g

620 g

 470 g

620 g

 ASTM D1922
 Seal Initiation Temperature2

2.0 mil(51 μm)

 178 ℉ 81.1 ℃ Dow Method
 Thermal  Vicat Softening Temperature 170 ℉ 76.7 ℃ ASTM D1525
 Melting Temperature (DSC) 205 ℉ 96.1 ℃ Dow Method
 Optical  Gloss (20℃, 2.00 mil(50.8 μm)) 134 134 ASTM D2457
 Clarity (2.00 mil(50.8 μm) 70.0 70.0 ASTM D1746
 Haze (2.00 mil(50.8 μm)) 1.30 % 1.30 % ASTM D1003
 Extrusion  Melt Temperature 40.8 ℉ 209 ℃
 Extrusion Nptes           Fabrication Conditions For Blown Film

  • Screw Size: 2.5 in.(63.5 mm); 24:1 L/D
  • Screw Type: Sterlex, Single Flight Double Mix
  • Die Gap: 70 mil (1.8 mm)
  • Melt Temperature:  408°F(209°C)
  • Output: 6 lb/hr/in. of die circumference
  • Die Diameter: 6 in.
  • Blow-Up Ratio: 2.5:1
  • Screw Speed: 50 rpm
  • Frost Line Height: 25 in. (635mm)

Notes

These are typical properties only and are not to be construed as specifications. Users should confirm results by their own tests.

1Modified rectangular test specimen.

2Temperature at which 1 lb/in. (4.4 N/25.4 mm) heat seal strength is achieved.

Heat Seal Strengths, Topwave HT Tester 0.5 S dwell, 40 psi bar pressure, pull speed 10 in./min (250 mm/sec).