Solumer 8705L
Solumer™ 8705L is an ethylene-octene copolymer produced via Nexlene™ technology. Solumer™ 8705L performs well in a wide range of general purpose thermoplastic elastomer applications and has excellent flow characteristics.
Description
Introduction
Solumer™ 8705L is an ethylene-octene copolymer produced via Nexlene™ technology.
Solumer™ 8705L performs well in a wide range of general purpose thermoplastic elastomer applications and has excellent flow characteristics.
Properties
| Typical Values | Unit | Test Method | ||
| Physical
Properties |
Density | 0.868 | g/cm3 | ASTM D792 |
| Melt index (2.16 kg @190℃) | 0.5 | g/10min | ASTM D1238 | |
| Mooney viscosity (ML1+4 @ 121℃) | 36 | MU | ASTM D1646 | |
| Mechanical
Properties 1 |
Tensile strength at break | 105 | kgf/cm2 | ASTM D6382 |
| Elongation at break | 800 | % | ASTM D6382 | |
| Tensile modulus (100% Elongation) | 32 | kgf/cm2 | ASTM D6382 | |
| Flexural modulus (1% secant) | 155 | kgf/cm2 | ASTM D790 | |
| Tear strength (Type C) | 46 | kgf/cm2 | ASTM D624 | |
| Hardness Shore A (1 sec)
Shore D (1 sec) |
74
23 |
–
– |
ASTM D2240
ASTM D2240 |
|
| Thermal
Properties |
Melting temperature | 62 | ℃ | SK Method |
| Glass transition temperature | -52 | ℃ | SK Method |
1 Evaluated using compression molded sample
2 Crosshead speed: 500 mm/min
Application
- General purpose thermoplastic elastomers
- Wire and cable
- Impact modification
- Footwear