FORTIFY™ Polyolefin Elastomer (POE) C5070D is an ethylene octene copolymer produced by solution polymerization using metallocene catalyst. This product is available as free flowing pellets. FORTIFY™ Polyolefin Elastomer (POE) C5070D is designed as a low density and high performance copolymer modifier to provide superior impact properties and flow characteristics.
Introduction
FORTIFY™ Polyolefin Elastomer (POE) C5070D is an ethylene octene copolymer produced by solution polymerization using metallocene catalyst. This product is available as free flowing pellets.
FORTIFY™ Polyolefin Elastomer (POE) C5070D is designed as a low density and high performance copolymer modifier to provide superior impact properties and flow characteristics.
Typical property values
| PROPERTIES | TYPICAL BALUES | UNITS | TEST METHODS | |
| POLYMER PROPERTIES | Density | 868 | kg/m³ | ASTM D792 |
| Melt Flow Rate (MFR)
at 190°C and 2.16 kg at 230°C and 2.16 kg |
5.0 11.0 |
g/10 min g/10 min |
ASTM D1238 ASTM D1238 |
|
| Mooney viscosity
ML 1+4, 121 °C |
8 | MU | ASTM D1646 | |
| MECHANICAL PROPERTIES(1) |
Tensile Properties
strength at break elongation |
6
1100 |
MPa % MPa |
ASTM D638 ASTM D638 ASTM D638 |
| Durometer Hardness shore A (1 second)
shore D (1 second) |
63
16 |
–
– |
ASTM D2240
ASTM D2240 |
|
| Flexural Modulus (1% Secant) | 10.8 | MPa | ASTM D790 A | |
| Tear Strength (Type C) | 35.3 | kN/m | ASTM D624 | |
| THERMAL PROPERTIES | Peak Melting Temperature | 62 | °C | SABIC method |
| Glass Transition Temperature, Tg | -52 | °C | SABIC method |
Application
- Impact modifier in thermoplastic olefin compounds
- Injection molded industrial and consumer durable goods
- Wire and cable extrusion and footwear
Features
- extrusion grade
- C8
Parameters
| Minimum Order Quantity: | 25kg |
| Price: | $1.5-$3 |
| Packaging Details: | 25kg/bag |
| Delivery Time: | 3-5 working days to departure port |
| Payment Terms: | TT/LC |
| Supply Ability: | 1000MT/Month |